    配资盘漆起殼脫皮的原因以及解決方案

    2018-10-12 09:09:02 慧投金融配资 閱讀

    配资盘漆起殼脫皮是配资盘最常見的問題,很多用户不知道起殼脫皮是什麼原因造成的?應該如何去解決?下面地坪漆廠家工程部就以地坪漆起殼脫皮兩大問題和大家談談:

    Epoxy floor paint shell peeling is the most common problem on the floor, many users do not know what causes the floor shell peeling? How should we solve this problem? The Engineering Department of the floor paint manufacturer will talk about the two problems of peeling off the floor paint.
    2-1P609151120412.jpg

    一、起殼

    1. Shell

    1、環氧面漆起殼

    1. Epoxy top coat.

    産生原因:面漆與批塗粘結層時未幹,有水、油、灰層等。

    The reason is that when the top coat is coated with the bonding layer, the water, oil and ash layer are not dried.

    解決方案:清除起殼層,再用打磨機進行打磨平整,批刮後重新滾塗面漆。

    Solution: remove the shell, then polish it with the grinding machine, then roll the top coat again after batching.

    2、整層環氧到表地起殼

    2, the entire layer of epoxy to the surface of the shell.

    産生原因:基礎未處理幹淨,打磨不到位;底漆沒有幹就施工了下一道工序;基礎不結實,未充分加固

    Reasons: foundation is not clean, grinding is not in place; primer is not dry on the construction of the next process; foundation is not solid, not fully reinforced

    解決方案:

    Solution:

    a、清理原環氧層,然後重新打磨好素地并清理幹淨後重新施工配资盘

    A, clean up the original epoxy layer, and then re polish the ground and clean up and re build the epoxy floor.

    b、 用打磨機打磨至硬質層,清理幹淨後用高固含樹脂加固素地,再進行後期施工。

    B. Grind the hard layer with a grinder, clean up and reinforce the vegetable land with high solid resin, and then carry out the later construction.

    3、局部起殼

    3. Local shell lifting.

    産生原因:施工造成,環境影響(可能漏油、漏雨等原因)

    Causes: construction, environmental impact (possible oil leakage, rain and other reasons)

    解決方案:對舊地面起殼區域進行沿邊局部“V”字型切割,

    The solution is to carry out partial "V" cutting on the edge of the old ground shell area.

    切割到混凝土堅硬部位,并清理垃圾、除塵,再整體打磨毛糙、平整,施工地坪。

    Cut to the hard part of the concrete, and clean up garbage, dust, and then the overall grinding rough, flat, construction floor.

    4、通道起殼

    4. Channel lifting

    解決方案:清除起殼層後用環氧樹脂進行加厚。

    Solution: remove the shell and thicken it with epoxy resin.

    5、耐磨地坪表面脫皮

    5. Surface peeling of wearable Floor.

    産生原因:混凝土泥沙、煤灰量大;施工錯誤;硬化劑骨料配比不合理

    The reason is: the volume of concrete and ash is large; the construction is wrong; the proportion of hardener aggregate is unreasonable.

    解決方案:重新更換混凝土;交叉打磨,撒料均勻,掌控施工時間節點;更換耐磨地坪材料。

    Solution: Replace the concrete; Cross-grind, sprinkle material evenly, control the construction time node; Replace the wear-resistant floor material.

    二、脫皮

    Two. Desquamation

    産生原因:素地松散脫皮;水汽産生脫皮;油污産生脫皮

    Causes: loose and desquamation; water vapor producing peeling; oil pollution peeling.

    解決方案:對素地進行加固處理;采用水性類的材料或處理防水;清理油污,解決将油導出渠道。

    Solution: to reinforce plain land; to use water-based materials or waterproof treatment; to clean up oil pollution, to solve the oil export channel.